SS430 is a low-carbon plain chromium,ferritic stainless steel without any stabilization of carbon and nitrogen with titanium or niobium.With 16% chromium,the steel has good crrosion resistance in soft corrosive environments and good oxidation resistance at elevator temperatures.Annealed SS430 is ductile and can be formed using a large variety of roll forming or mild stretch-bending operations as well as the more common drawing and bending operations.


SS430 has limited weldability and should not be used in the as-welded condition for dynamic or impact loaded structures.SS430 can form martensite in the heat affected zone of weldments,which may adversely affect the mechanical properties an these zones.Applications involving welded SS430 are generally limited to a maximum thickness of 3mm.


Corrosion Resistance:SS430 has good corrosion resistance in a wide varitely of corrosive environments including nitric acid and some organic acids.It is generally used for highly polished applications and in mild atmospheres such as for food processing and dairy equipment.Atmospheric corrosion resistance is good,although in highly polluted or marine environments staining may occur.


Annealing:Annealing is achieved by heating to above 760℃ and 830℃for 90 minutes per 25mm thickness followed by air quenching.Controlled atmospheres are recommended in order to avoid excessive oxidation of the surface.


Welding:SS430 is prone to brittle characteristic in the heat-affected zone of weldments due to formation of martensitic phase.Thw tensile,fatigue and thoughness properties in the welded condition are relatively poor.So SS430 should not be used for applications where tensile or dynamic loading will be experience.Edge welds are not recommended for SS430.The use of austenitic filler metals such as types 309S or 316L will improve the ductility of welds to some extent but all welding procedures should nevertheless endeavor to maintain minimum heat inputs.The weld discoloration should be removed by pickling and p[assivating to restore maximum corrosion resistance.


Grade

430 stainless steel coil        

Thinckness

0.3-6mm

Widthness

1000mm, 1219mm, 1524mm or as customized

Brand name

TISCO,BAO Steel,ZPSS,BAO XIN,LISCO..

Standard

JIS, AISI, ASTM, GB, DIN, EN ,etc.

Finish

2B, Hairline, No.4, BA, 8K mirror, etc.

Certification

SGS

Packaging

Standard exporting packing;   seaworthy package.

MOQ

5 Tons


Chemical Composition and mechanical properties:

430

C

Si

Mn

P

S

Ni

Cr

≤0.12

≤0.75

≤1.00

≤0.04

≤0.03

≤0.6

16.00~18.00

tensile strength σb     (MPa)

yield strength   σ0.2(MPa)

elongation    δ5(%)

Hardness   HB

450

205

22

200

/static/upload/images/50f0c79f013a512c8e69a127e2acb25d.jpg

Tolerance range of 430 cold rolled   stainless steel coil

Thickness

Large  Tolerance

Normal   Tolerance

Small   Tolerance

No   Tolerance

0.4MM

0.3-0.32

0.33-0.37

0.37-0.39

≥0.39

0.5MM

0.4-0.42

0.43-0.47

0.47-0.49

≥0.49

0.6MM

0.5-0.52

0.53-0.56

0.57-0.59

≥0.59

0.7MM

0.6-0.62

0.63-0.67

0.67-0.69

≥0.69

0.8MM

0.7-0.72

0.73-0.77

0.74-0.79

≥0.79

0.9MM

0.8-0.82

0.83-0.87

0.87-0.89

≥0.89

1.0MM

0.89-0.9

0.91-0.94

0.94-0.99

≥0.99

1.2MM

1.02-1.08

1.09-1.15

1.16-1.18

≥1.18

1.5MM

1.32-1.38

1.39-1.45

1.46-1.48

≥1.48

2.0MM

1.72-1.79

1.8-1.86

1.87-1.9

≥1.9

2.5MM

2.23-2.36

2.32-2.42

2.42-2.47

≥2.48

3.0MM

2.7-2.77

2.78-2.85

2.85-2.9

≥2.9

 

Tolerance range of 430 hot rolled   stainless steel coil

Thickness

Large  Tolerance

Normal   Tolerance

Small   Tolerance

No   Tolerance

3.0MM

2.6-2.75

2.75-2.85

2.86-2.9

≥2.9

4.0MM

3.5-3.6

3.6-3.75

3.76-3.95

≥3.95

5.0MM

4.5-4.6

4.6-4.75

4.75-4.95

≥4.95

6.0MM

5.4-5.6

5.6-5.75

5.75-5.85

≥5.85

8.0MM

7.3-7.5

7.5-7.65

7.65-7.85

≥7.85

10.0MM

9.2-9.3

9.3-9.6

9.6-9.85

≥9.85

12.0MM

11.1-11.2

11.2-11.6

11.6-11.85

≥11.85

14.0MM

13.1-13.2

13.2-13.6

13.6-13.85

≥13.85


Feedback from contact with us
Contact us