5005 aluminum sheet/coil of WILKE is certificated to ASTM, EN as well as JIS, etc. and it can be cut to size at customers’ need. Mg is the principal element in the 5005 aluminum sheet/coil and when it used as main alloying element or combined with Mn, high strength and no-heat treatable properties can be realized. 5005 aluminum sheet/coil of WILKE has many tempers available, such as 5005-H12, 5005-H14, 5005-H16, 5005-H18,5005-H22, 5005-H24, 5005-H32, 5005-H34, 5005-H36, 5005-H38, etc.
Elements | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Others | Al | ||
Content | 0.3 | 0.7 | 0.2 | 0.2 | 0.5-1.1 | 0.1 | 0.25 | - | 0.15 | Remain | ||
Alloy Temper | Specified thickness | Tensile strength | Yield strength | Elongation | ||||||||
(MPa) | (MPa) | (%) | ||||||||||
5005-H34 or 5005-H24 | 0.2~0.63mm | 138.179 | Min104 | min 3 | ||||||||
0.63~1.2mm | min 4 | |||||||||||
1.2~6.3mm | min 5 | |||||||||||
6.3~50mm | min 8 | |||||||||||
5005-H32 or 5005-H22 | 0.2~600mm | 118-158 | Min83 | min 3 | ||||||||
5005-H14 | 145-186 | min118 | min1 | |||||||||
Applications
The main content of 5005 aluminum sheet/coil is Fe, Mg and Si, thus, it has good weld-ability and resistance to correction (especially when anodized), which resulting in suitable for marine applications. 5005 aluminum sheet/coil is also a non-heat treatable alloy and it can be strengthened (hardened) by cold working. However, hot working should not normally be necessary. Besides, it scores well in formability, especially in softer tempers. The machinability of 5005 aluminum sheet/coil is generally fairly poor. 5005-H34 and 5003-H38 can be machined, but with much more difficult than many other aluminum alloys.